- AS/NZS IS0 17632-B - T492T8-1NA-U H10
- AWS A5.20: E71T-8JD H8
- CLASSIFICATION
- AS/NZS IS0 17632-B - T492T8-1NA-U H10
- AWS A5.20: E71T-8JD H8
- SPECIFICATIONS
- Typical All Weld Metal Chemical Analysis
- C Mn Si P S AI Fe
- 0.19 0.51 0.17 0.009 0.006 0.51 Bal
- Typical All Weld Metal Mechanical Analysis
- Yield Strength Tensile Strength Elongation CVN Impact Values
- 469 MPa 579 MPa 28% 68J @ -20C
- 54J @ -30C
- 42J @ -40C
LOW HYDROGEN T-8 SELF-SHIELDED, ALL POSITIONAL FLUX CORED WIRE, PRODUCING A STABLE ARC AND FLAT BEAD PROFILE.
Typical Applications
Specifically designed for increased productivity and high deposition rates on challenging structural steel erection, heavy equipment repair, mining equipment, bucket repairs, storage tanks, pipe spooling, ship construction and site work applications.
New sealed poly package with a VCI (Vapour Corrosion Inhibitor) coating
Superior rust and corrosive protection
Easy To Open
Environmental friendly disposal
Description
Low hydrogen T-8 self-shielded, all positional flux cored wire, producing a stable arc and flat bead profile, especially suited for vertical-up welds at high currents with excellent mechanical properties and a tensile strength of 490 MPa.
Capable of depositing X-ray quality welds, making it highly suitable for critical welding applications requiring a high degree of crack resistance due to its low diffusible hydrogen levels, less than 6.7ml per 100g of weld metal deposited.
XLR-8 has been designed for single and multi-pass welding applications with improved productivity in out-of-position welding, offering high impact strength of 42J at sub zero temperatures to -40C.